Chen Wei1; Li Shiyu1; Yin Jiangming1; Luo Wenyong1; Mo Qi1; Ke Yili1; Hu Fuming1; Dan Rong1

doi:10.13756/j.gtxyj.2012.06.001

您当前的位置：

首页 >

文章列表页 >

Fabrication of high performance PMF and research on its key application characteristics

- Fabrication of high performance PMF and research on its key application characteristics
- Study on Optical communication Issue 6, Pages: 42-44(2012)
- 作者机构：
  
  1. 光纤通信技术和网络国家重点实验室
  2. 烽火通信科技股份有限公司
- 作者简介：
- 基金信息：
- DOI：10.13756/j.gtxyj.2012.06.001
  CLC： TN253
- Published：2012，
扫描看全文
[1]陈伟,李诗愈,殷江明,罗文勇,莫琦,柯一礼,胡福明,但融.高性能保偏光纤制备及关键应用特性研究[J].光通信研究,2012(06):42-44.

Chen Wei1, Li Shiyu1, Yin Jiangming1, et al. Fabrication of high performance PMF and research on its key application characteristics. [J]. (6):42-44(2012)
[1]陈伟,李诗愈,殷江明,罗文勇,莫琦,柯一礼,胡福明,但融.高性能保偏光纤制备及关键应用特性研究[J].光通信研究,2012(06):42-44. DOI： 10.13756/j.gtxyj.2012.06.001.

Chen Wei1, Li Shiyu1, Yin Jiangming1, et al. Fabrication of high performance PMF and research on its key application characteristics. [J]. (6):42-44(2012) DOI： 10.13756/j.gtxyj.2012.06.001.

摘要

开发了一种高性能PMF（保偏光纤）的制造工艺

并制备出包层直径为80μm的细径高性能PMF。试验结果表明

该光纤具有优良的全温（-50～85℃）偏振串音性能

光纤全温偏振串音变化典型值为3.232dB

具有良好的抗弯曲性能和良好的端面研磨性。

Abstract

In this letter

a new manufacturing process for high-performance Polarization Maintaining Fiber（PMF） is developed and the PMF with 80 μm cladding diameter fabricated.The experimental results show that this fiber has fine polarization cross-talk performance in the temperature range from-50 to 85 ℃

with the typical cross-talk change value of 3.232 dB

and good bending resistance and abrasive fiber ends.

关键词

保偏光纤光纤陀螺特种光纤制备应用

Keywords

PMFfiber-optic gyroscopespecialty fiberfabricationapplication

references

更多指标>

Views

209

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research on the Ultraslim PMF Technologies

The Optical Generation of Monocycle and Doublet UWB Signals Based on the Polarization Modulation

Design and applications of PMDE in high-rate fiber-optic communication systems

Design and fabrication of high numerical aperture and large mode-field Ytterbium-doped photonic crystal fibers

Applications of POF in high speed LAN

Related Author

No data

Related Institution

Ruiguang Telecommunication Technologies Co., Ltd.

College of Information Engineering,Communication University of China

Liaocheng University

Key Laboratory of Optical Communication

Commercial Mechanics School

⁰